铅酸密封蓄电池修复必备桂林市同声电器厂编 目  录 一、电池结构原理简介········································· 2二、补液标准·························································· 3三、充电标准·························································· 3四、正负脉冲·························································· 3五、小电流修复充电············································· 4六、电池封盖标准················································· 4七、电池配组·························································· 4八、电池液配制······················································ 5九、判断可修复电池············································· 5十、电池自放电原因············································· 6十一、修理蓄电池程序········································· 6十二、短路电池单块12V修理··························· 7十三、判断短路电池············································· 8十四、电池检测方法············································· 8十五、修理电池工具············································· 8一、铅酸密封电池简介1、铅酸密封电池与普通蓄电池结构几乎一样，它是在普通型电池基础上改进了一大步，主要增设了气压阀、防电液浪动石棉纸、内紧密化、外型精制化，它比普通电池寿命增长1-2倍。2、密封电池单隔解剖图电压为2V二、补液标准1、电池在补液时不得过多，充电时会产生大量的气体，补液要留有一定的空间，电液超过极板5mm即可。2、电池补液必须用“蒸馏水、标准液”。禁用矿泉水及自来水。3、电池加蒸馏水后 “经修复”可恢复容量，加(比重：1.25-1.33)标准液可在原加蒸馏水基础上提高10-20%容量。三、电池充电标准1、例12V12Ah电池充电，充电的电流为电池Ah的十分之一，也就是1.2A电流，如充电电流过大时间过长电池外部过发热，会减少电池的使用寿命。2、电池在充电时视看电压表，12V电池充满电电压为16-17V。也可用比重计测电液比重，例：电液比重1.25，充满电后比重为1.27。四、正负脉冲1、修复电池过程中使用正负脉冲对电池极板去硫化，使电池极板恢复活性。2、正负脉冲为低频率，都低于50HZ，以下简称为快脉冲、中脉冲、慢脉冲。慢脉冲指针摆动的幅度大；中脉冲指针摆动的幅度小；快脉冲指针摆动的幅度更小。五、小电流修复充电1、在修理电池中充电时应采用高电压，小电流对电池进行修复充电，小电流充电使电池极板匀衡蓄电，充电时间越长对电池蓄电越好，电池极板恢复活性也越好，小电流充电也是恢复电池容量的重要环节。六、电池封盖标准1、修理电池时必须撬盖补液，修复后加以密封，密封得好电池寿命就长，没密封好电池寿命就短。2、没密封好电池在充电时大量失水，电池失水后容量减少，由于充电时电池发热，产生大量的水蒸气跑入空气中。修复后必须密封好。3、电池为什么要密封好密封好的电池在充电时电池发热产生水蒸气体、气压，要在超压过程中才能跑出，它由水蒸气转化成水珠又回落下去，所以密封好的电池几乎失水少，容量保持不变状况。七、电池配组1、修复的电池经检测后实行配组，由于电池是串联使用，电池的电压可直接影响到电动车的额定输入电压，所以将电池组合配组使用。2、电池配组大多采用负载配组，也就是电池受负载后电压的读数来作配组标准。例12V12Ah电池用30-60A4电流作负载，这样将高读数电池与高读数电池配合起来串联成高电压使用。3、放电计时配组，将修好的电池单块12V在放电仪器上计时放电，把放电时间相等的电池组合使用。八、电池液的配制1、配制电池液需要用塑料桶及防腐桶、塑料搅拌棍，比重计、蒸溜水、浓硫酸。2、配制方法将蒸溜水先倒入塑料桶中，后慢慢的加入浓硫酸，搅拌测比重，标准液为1.25，补充液为1.1-1.16之间都可。3、配液注意事项●浓硫酸倒入蒸溜水中，禁止将水倒入硫酸中。●配制时备用清水，如有浓硫酸沾入身上，沾处浸入清水中清洗即可。九、判断可修复电池1、电池在备修理时首先就是负载检测电池，量出电压读数，一组电池内应有一块读数最低，将最低的电池打上计号。2、放完电后补液，脉冲充电修复，视看最差读数电池充电能恢复在16-17V之间，能恢复证明电池还是好的也即可使用。3、断隔电池，极板严重脱粉不能修复，修复充电时电压读数不能恢复的也不能修复。十、电池自放电原因 充满电的电池不使用、放置5-10天，电池电压大幅度下降，证明补的液体中有大量的矿物质，导致电池产生自放电现象，严重可使电池废掉。十一、修理蓄电池程序例：10A电流修复电池修复蓄电池流程 →   →    →    →    →    →    →    → 低容量电池  需二次修复   〈一〉、修理电池前期工作： 例：一组电池经负载检测，各电压读数电池分别打上记号，电池进行过放电到0—2V,用万用表测量单块电池，待每块电池电压平衡后才取下正负极夹具补液。〈二〉、补液事项： 补 液比 重修复容量比较电池补液后浸泡30分钟1蒸 馏 水1一般2标 准 液1.25比较高3高浓度标准液1.35特别高〈三〉、电池慢速修复方法：1、将放完电补好液的电池串联组合１－12块，修复6电流为10A加正负脉冲。 2、10A大电流加正负脉冲对电池进行激活，激活时间：20AH激活1小时，12AH激活30分钟。 3、激活后的电池用小电流维护修复，20AH用1-2.5A电流充电8小时，12AH电池用0.5-1.5A电流充电8小时，至电池电压每块上升到16-17V满电即可。〈四〉、电池快速修复方法：1、将放完电补好液的电池串联，用10A电流加正负脉冲激活90分钟、间隔半小时后再用10A电流激活至电池电压每块上升到16—17V即可，电池容量为70%左右。2、激活好的电池用小电流维护修复，20AH用2A电流，12AH用1.5A进行2-4小时维护修复直至电压上升16-17V满电即可。3、以上快、慢修复的电池经计时放电检测。4、激活电池注意事项：电池从0V激活，激活电流10A，电压很快上升。当电池在一定蓄电量时，电池内产生发热量，掌握和控制热量、温度是修理电池的关键。当电池温度过高（60℃）就会烧坏电池，也就是说电池越修越差，越修越坏。十二、短路电池单块12V修理1、例：单块12V—12AH至20AH电池，大电流使用为10A加正负脉冲，将放至0V的电池激活，在激活过程中，电池某隔短路处很快被大电流溶断，当短路处溶断后隔数电压上升，电池总体电压上升为12V，证明短路处修理好。十三、判断短路电池12V电池在10A电流修复充电时单隔出现早冒泡（冒泡处温度比其它隔温度高）证明是单隔短路。如电池单隔是轻微短路在大电流修复时很快会溶断短路处，短路处溶断后电池即可恢复正常修复。十四、电池检测方法将修复好的电池经过放电计时检测，12V12AH用10A电流计时放电时间为60分钟，12V20AH用10A电流计时放电，放电时间为120分钟，以上放电时间为新电池容量。 十五、修理电池工具1、充放电修复仪器一台，快速过放电仪一台，容量测试仪一台，连接电池夹具。2、抽液大小注射器各一支，比重计一支、玻璃试管一支。3、撬盖工具一支，电池联接线扳手及螺丝刀。4、密封胶水、环氧树脂、A、B胶，502胶水。5、电池液配制器具，塑料桶、塑料搅拌棍，蒸溜水、浓硫酸。制造商：桂林市金同声电器有限公司(原桂林市同声电器厂）厂  址：广西桂林市高新区穿山东路9号电  话：0773-2195762 ，2195551 传  真：0773-2195551       竭诚欢迎您前来洽谈，代理产品销售面议。        制造：桂林市金同声电器有限公司        地址：桂林市高新区穿山东路9号        热线：0773-2195762，2195551        网址：www.tsdq168.cn